| Customization: | Available |
|---|---|
| Feature: | Photodegradable |
| CAS No.: | 9002-86-2 |
|
Still deciding? Get samples of US$ 1/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
|
Product Name
|
Polyvinyl Chlorides Resin S700 S1000
|
|
Brand Name
|
Sinopec
|
|
Appearance
|
White stable powder
|
|
Particle size
|
60-250um
|
|
Apparent Density
|
0.4-0.6g/ml
|
|
Physical and
chemical properties
|
100ml cyclohexanones contains 0.5g resin in dilute solution viscosity 80-160ml/ g, 100g resin absorbs 20-30 grams of plasticizer at room temperature.
|
|
Main use
|
It can be used to produce soft films, artificial leather, sheets, pipes, profiles, corrugated pipes, cable protection tubes,packaging films, hoses, shoe soles and various soft sundries.
|
|
PVC RESIN S-700
|
|||
|
Grade
|
Measured Value
|
||
|
Specification
|
STANDARD
|
RESULT
|
|
|
Item
|
|||
|
Appreance
|
White powder
|
White powder
|
|
|
Impurity Particle Number
|
≤16
|
10
|
|
|
Mass fraction of Volatile Matter (including water),%
|
≤0.3
|
0.14
|
|
|
Apparent Density,g/mL,≥
|
0.54-0.62
|
0.61
|
|
|
Reduce on Sieve,%
|
250umSieve Mesh ≤Sieve,
|
1.6
|
0
|
|
63umSieve Mesh ≥Sieve,
|
97
|
97
|
|
|
"Fish Eye"/400cm²≤
|
≤16
|
7
|
|
|
100g Resin Plasticizer Absorption,g
|
≥14
|
16.4
|
|
|
Whiteness(160ºC,10min),%≥
|
≥75
|
70
|
|
|
Average degree of polymerization
|
650-750
|
700
|
|
|
Residual Vinyl Chlorides Monomer Content,ug/g
|
≤3
|
1
|
|
|
PVC RESIN S-1000
|
|||
|
Grade
|
Measured Value
|
||
|
Specification
|
STANDARD
|
RESULT
|
|
|
Item
|
|||
|
Appreance
|
White powder
|
White powder
|
|
|
Impurity Particle Number
|
≤16
|
10
|
|
|
Mass fraction of Volatile Matter (including water),%
|
≤0.3
|
0.14
|
|
|
Apparent Density,g/mL,≥
|
0.5-0.58
|
0.54
|
|
|
Reduce on Sieve,%
|
250umSieve Mesh ≤Sieve,
|
1.6
|
0
|
|
63umSieve Mesh ≥Sieve,
|
97
|
98
|
|
|
"Fish Eye"/400cm²
|
≤12
|
6
|
|
|
100g Resin Plasticizer Absorption,g
|
≥20
|
24.8
|
|
|
Whiteness(160ºC,10min),%≥
|
≥78
|
84.7
|
|
|
Average degree of polymerization
|
970-1070
|
1010
|
|
|
Residual Vinyl Chlorides Monomer Content,ug/g
|
≤3
|
0.1
|
|