Suspension Process PVC S1000 for Pipes and Windows

• Customization: Available
• Feature: Photodegradable
• CAS No.: 9002-86-2
• Model NO.: S700 S1300 S1000 S1050p
• Formula: (C2h3cl)N
• EINECS: 208-750-2
• Material: Polyvinyl Chloride/PVC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Blow Molding
• Color: White
• CAS No: 13463-67-7
• Mf: (C2h3cl)N
• Application: Piping, Film and Sheeting, PVC Fibers
• Appearance: White Powder
• Model Number: S700 S1000 S1300
• Transport Package: 25kg or as Your Required
• Specification: S700 S1000 S1300
• Origin: China
• HS Code: 3904109090
• Production Capacity: 5000mts Per Month

Product Description

Product Description

Polyvinyl chlorides is high molecular compounds polymerized with structural element as CH2-CHCLn,degree of polymerization usually as 590-1500.In the process of re-polymerization ,affected by kinds of factors such as the polymerization process, reaction conditions, reactant composition, additives etc.it can produce eight different types of PVC resin performance is different.

Product Name	Polyvinyl Chlorides Resin S700 S1000
Appearance	White stable powder
Particle size	60-250um
Apparent Density	0.4-0.6g/ml
Physical and chemical properties	100ml cyclohexanones contains 0.5g resin in dilute solution viscosity 80-160ml/ g, 100g resin absorbs 20-30 grams of plasticizer at room temperature.
Main use	It can be used to produce soft films, artificial leather, sheets, pipes, profiles, corrugated pipes, cable protection tubes,packaging films, hoses, shoe soles and various soft sundries.

Product Parameters

PVC RESIN S-700
Grade		Measured Value
Specification		STANDARD	RESULT
Item
Appreance		White powder	White powder
Impurity Particle Number		≤16	10
Mass fraction of Volatile Matter (including water),%		≤0.3	0.14
Apparent Density,g/mL,≥		0.54-0.62	0.61
Reduce on Sieve,%	250umSieve Mesh ≤Sieve,	1.6	0
	63umSieve Mesh ≥Sieve,	97	97
"Fish Eye"/400cm²≤		≤16	7
100g Resin Plasticizer Absorption,g		≥14	16.4
Whiteness(160ºC,10min),%≥		≥75	70
Average degree of polymerization		650-750	700
Residual Vinyl Chlorides Monomer Content,ug/g		≤3	1

 

PVC RESIN S-1000
Grade		Measured Value
Specification		STANDARD	RESULT
Item
Appreance		White powder	White powder
Impurity Particle Number		≤16	10
Mass fraction of Volatile Matter (including water),%		≤0.3	0.14
Apparent Density,g/mL,≥		0.5-0.58	0.54
Reduce on Sieve,%	250umSieve Mesh ≤Sieve,	1.6	0
	63umSieve Mesh ≥Sieve,	97	98
"Fish Eye"/400cm²		≤12	6
100g Resin Plasticizer Absorption,g		≥20	24.8
Whiteness(160ºC,10min),%≥		≥78	84.7
Average degree of polymerization		970-1070	1010
Residual Vinyl Chlorides Monomer Content,ug/g		≤3	0.1

 